In the course of this work the reduction of emissions of free formaldehyde from the finished plywood is identified, as well as an increase in shear strength to the adhesive layer. Obtained effects in the manufacture of plywood are due to the use of adhesive compositions using natural zeolite sorbent filler – clinoptilolite, previously activated in various electromagnetic fields (fields of over high frequency and weak pulsed magnetic fields). The optimal processing modes of minerals with electromagnetic fields are defined, providing an optimum ratio of values of free formaldehyde emission levels and shear strength to the adhesive layer. The results indicate the possibility of industrial use of the developed techniques.
environmentally friendly plywood, natural filler, adhesive composition, formaldehyde, shear strength to the adhesive layer, electromagnetic fields, microwave, weak pulsed magnetic fields
В настоящее время древесные плитные материалы (Д11М) получили широкое распространение в строительстве, деревообработке и мебельном производстве, изготовлении отделочных материалов и других отраслях производства. Изготовление разнообразных древесных плитных материалов (фанера, ДСтП, ДВП и др.) проводится с применением клеевых композиций. При ежегодном возрастании спроса на Д11М к ним предъявляются все более жесткие требования по физико-механическим и экологическим показателями, которые должны соответствовать не только российским, но и зарубежным стандартам. Это обусловлено так же стремлением отечественных производителей выйти на европейский и мировой рынок строительных материалов с привлечением российских компаний к совместным проектам с зарубежными производителями.
Необходимость увеличения объемов производства Д11М связана с планами Правительства России по развитию строительства. Согласно правительственному постановлению "О федеральной целевой программе "Жилище" на 2011...2015 годы", темпы строительства жилья должны быть увеличены в 1,5 раза и составлять 90 миллионов м в год (по материалам сайта www.fcpdom.ru).
Таким образом, целью данной работы является создание экологически безопасных древесных плитных материалов, обладающих эксплуатационными характеристиками, которые отвечают предъявляемым стандартам качества, как в России, так и за рубежом.
В большинстве современных клеевых композитных связующих, по данным, представленным Куликовым В.А. и Чубо-вым А.Б., используются минеральные, органические или синтетические наполнители для улучшения физико-механических характеристик. К неорганическим наполнителям относятся каолин, мел, асбест, гипс, сажа, тонко размолотое стекло, высокодисперсные металлические порошки, цеолиты, природные глины и другие. Эти наполнители не набухают в воде и не растворяются в ней, хорошо закрывают сосуды древесины, тем самым, препятствуя просачиванию клея через тонкие слои шпона. Они снижают влияние толщины клеевого слоя на прочность клеевого соединения. Неорганические наполнители традиционно применяются только в качестве регулятора вязкости используемого связующего, обеспечивая тем самым снижение его расхода при производстве ДИМ. Природа наполнителя влияет на технологические свойства клеёв. Например, наличие ионов алюминия в неорганическом наполнителе способствует, согласно работе
1. Prirodnye tseolity / G.V. Tsitsish-vili, T.G. Andronikashvili, G.N. Kirov [i dr.]. M.: Khimiya, 1985. 224 s.
2. Bel´chinskaya L.I. Kompleks pri-rodozashchitnykh tekhnologicheskikh resheniy pri ispol´zovanii lakovykh kompozitsiy i mol v derevoobrabatyvayushchey promyshlennosti: diss. ... dokt. tekhn. nauk. Voronezh, 1996. 534 s.
3. Neutralization of waste water from formaldehyde and heavy metals by activated clinoptilolite in electromagnetic fields / M.V. Anisimov, L.I. Belchinskaya, K.V. Strokova, [et. al]. Adhesives in woodworking industry : Zbornic referatov XXI International Sympo-zium, 26-28.06.2013. Zvolen: Technical University inZvolen, 2013. PP.80-85.
4. Bel´chinskaya L.I., Anisimov M.B. Vliyanie nanonapolniteley kleevoy kompozitsii dlya obespecheniya ekologicheskoy bezopasnosti fanery. Nauchnyy vestnik. Stroitel´stvo i arkhitektura. 2012. №1.
5. Chelishchev N.F., Berenshteyn B.G., Volodin V.F. Tseolity - novyy tip mineral´nogo syr´ya. M.: Nedra, 1987. 176 s.
6. Khodosova NA., Bel´chinskaya L.I., Anisimov M.V. Sorbtsionnye izmeneniya prirodnogo tseolita i iskusstvennogo kremnezema pri razlichnykh vidakh fizicheskoy obrabotki. Sorbenty kak faktor kachestva zhizni i zdorov´ya : materialy IV mezhdunar. nauch. konf. (Belgorod, 24-28 sentyabrya 2012 g.). Belgorod: ID «Belgorod», 2012. S. 171-176.
7. Anisimov M.V., Bel´chinskaya L.I. Elektromagnitnaya obrabotka nanorazmer-nykh napolniteley dlya proizvodstva kleenykh materialov. Innovatsionnye tekhnologii i materialy (ITM-2011): sb. dok. vseross. nauch.-prakt. konf. studentov, aspirantov i molodykh uchenykh (g. Voronezh, 15-16 noyabrya 2011 g.) / redkol.: A.D. Pova-lyaev [i dr.]. Voronezh: FGBOU VPO «Voronezh, gos. tekhn. un-t», 2011. S. 194-197. 1 elektron, opt. disk (CD-R).
8. Aktivatsii klinoptilolita v elektromagnitnykh polyakh dlya ochistki stochnykh vod ot formal´degida / M.V. Anisimov, L.I. Bel´chinskaya, Yu.S. Strukova, [i dr.]. Aktual´nye voprosy khimicheskoy tekhnologii i zashchity okruzhayushchey sredy: sb. mat. vseros. konf. 25-26 oktyabrya 2012 g. Cheboksary: Izd-vo Chuvash, un-ta, 2012. S.39-40.
9. Anisimov M.V., Khodosova N.A., Bel´chinskaya L.I. Fizicheskaya obrabotka kak faktor aktivatsii sorbtsionnoy sposobnosti klinoptilolita. Otdel´nyy dopolnitel´nyy sbornik materialov: Ekologiya Rossiiskoy Federatsii, obzor problem, dinamiki i tekushchego sostoyaniya okruzhayushchey sredy. Perm´: OOO «Stil´-MG» po zakazu FGBU «Tsentral´noe byuro informatsii Minprirody Rossii», 2013.S. 177-181.
10. Anisimov M.V.Elektromagnitnaya obrabotka nanonapolniteley dlya proizvodstva kleenykh materialov. Innovatsionnye razrabotki molodykh uchenykh Voronezhskoy oblasti na sluzhbu regiona: sb. dok. Regional´noy nauch. konf. studentov, aspirantov i molodykh uchenykh, Voronezh, 16-17 aprelya 2012 g. Voronezh: Fond sodeystviya razvitiyu malykh form predpriyatiya v nauchno-tekhnicheskoy sfere; Prav. Vor. Obl.; VITTs, 2012. S. 113-114.
11. Liptakova E., Sedliacik M. Chernia a aplikaciapomocnych latok v drevarskom priemysle. Bratislava, 1989. 520 s.
12. Razin´kov E.M., Murzin B.C., Lavlinskaya O.V. Tekhnologiya kleenykh materialov i drevesnykh plit. Izgotovlenie i ispytanie materialov: metod, ukazanie k vypolneniyu laboratornykh rabot dlya studentov spetsial´nosti 260200 (250303) -Tekhnologiya derevoobrabotki. Voronezh: Fed. agentstvo po obrazovaniyu, GOU VPO «VGLTA», 2007. 52 s.