COMPOSITE MATERIAL MECHANICAL PROPERTIES EVALUATION USING A DYNAMIC INDENTATION METHOD
Journal: NDT WORLD
Volume 19 № 4
, 2015
Rubrics: NDT OF COMPOSITES
Authors:
2.
Mescherskiy filial FGBNU "VNIIGiM im. A.N.Kostyakova"
Russian Federation
Russian Federation
Type:
Article
Pages:
from 24
to 27
Status:
Published
Received:
13.12.2016
Accepted:
13.12.2016
Published:
13.12.2016
Language:
Russian
Keywords:
dynamic indentation, modulus of elasticity, reinforcement, hardness
Abstract (English):
Introduction. Dynamic indentation method is considered promising in testing mechanical properties of composite materials. Today, composite materials are widely used in the aviation and aerospace industries. That’s why, testing of mechanical properties of composite materials is so vital. Method. To register the current velocity of the indenter penetration into the tested composite material, use is made of a device that enables a contactless measurement of the indenter penetration velocity after the indenter strikes the tested product. The data obtained is digitized and sent to a PC for further processing. Results. The experiment produced "contact force – penetration depth" diagrams for three test zones in the prepared samples. The analysis showed that the non-uniformity of mechanical properties in the rod’s butt end and side surface is stipulated by pores and microcracks, and this is confirmed by computer tomography. It is shown that dilaminations, microcracks and local non-uniformity zones in the structure tell on the elasticity modulus measurements. Conclusions. The dynamic indentation method allows one to test composites at the micro- and macrostructural level, as well as compute their integral mechanical properties.
Introduction. Dynamic indentation method is considered promising in testing mechanical properties of composite materials. Today, composite materials are widely used in the aviation and aerospace industries. That’s why, testing of mechanical properties of composite materials is so vital. Method. To register the current velocity of the indenter penetration into the tested composite material, use is made of a device that enables a contactless measurement of the indenter penetration velocity after the indenter strikes the tested product. The data obtained is digitized and sent to a PC for further processing. Results. The experiment produced "contact force – penetration depth" diagrams for three test zones in the prepared samples. The analysis showed that the non-uniformity of mechanical properties in the rod’s butt end and side surface is stipulated by pores and microcracks, and this is confirmed by computer tomography. It is shown that dilaminations, microcracks and local non-uniformity zones in the structure tell on the elasticity modulus measurements. Conclusions. The dynamic indentation method allows one to test composites at the micro- and macrostructural level, as well as compute their integral mechanical properties.
Keywords:
dynamic indentation, modulus of elasticity, reinforcement, hardness
dynamic indentation, modulus of elasticity, reinforcement, hardness
1. Oliver W.C., Pharr G.M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 1992. V. 7. No. 6. P. 1564-1583.
2. Bulychev S.I., Alekhin V.P. Ispytanie materiala nepreryvnym vdavlivaniem indentora [Con-tinuous indentation material test]. Мoscow, Mashinostroenie, 1990, 224 p. (in Russ).
3. Rudnitskiy V.A., Rabtsevich A.V. Dynamics indention method for metal mechanical characteristics evaluation. Russian J. Nondestructive Testing. 1997, no.4, pp. 75-81 (in Russ.).
4. Vriend N. M., Kren A. P. Determination of the viscoelastic properties of elastomeric materi-als by the dynamic indentation method. Polymer Testing. 2004. V. 23. No. 4. P. 369-375.